Why Heated Clothing

Cold weather is uncomfortable and potentially dangerous. Heating clothing,such as a battery heated jacket or vest or heated gloves,can transform an uncomfortable,potentially hazardous experience into warm comfort-allowing you to enjoy an outdoor lifestyle longer.

Mainiko heated clothing create core body warmth only when you need it. You can turn down or turn off the heating when exercising to prevent overheating and turn it on again during rest periods to prevent an after-exercise chill. If the weather is a little warmer,detach the controller and battery easily, and wear it as regular apparel.
Heated Clothing such as a battery heated vest, or jacket,or battery heated gloves add to your body’s natural ability to generate heat. Adjusting the heat intensity helps you stay warm and comfortable in a wider range of temperatures.Also ,heated clothing keeps you warmer without using up the needed resources your body needs to maintain other healthy body function.

“There is no bad weather,only bad clothing”
Mainiko heated clothing is ideal for intermittent physical winter activities or just to stay warm outside , whatever your activity. Focus on enjoying yourself instead of how long you can with stand the cold.

Staffing service system approach

Staffing service must be carried out in a systematic manner, ie organizational goals and plans are the basis for organizational structure design, and the existing and expected organizational structures determine the number and type of managers required. Through the analysis of the needs of supervisors, in the process of recruitment, selection, placement and promotion, the use of external and internal sources of talent, as well as the assessment, training and training of supervisors. Appropriate staffing helps to guide and lead the work. Similarly, the selection of good executives will also facilitate control. Staffing requires an open system approach that is implemented within the organization and, in turn, with the external environment. Internal factors of the organization should be taken seriously, and without proper remuneration, it is impossible to keep attracting excellent executives. The external environment cannot be ignored, otherwise it will hinder the normal development of the organization.

What is staffing service?

Staffing service is the provision of all personnel in the organization, including both the staff of the supervisor and the staff of non-executives. The basic methods used and the basic principles followed are similar.

The staffing in management school refers to the appropriate and effective selection, training and evaluation of the supervisors. The purpose is to equip the appropriate personnel to enrich the various positions stipulated in the organization to ensure the normal operation of the organization. To achieve the stated goals of the organization.

The traditional view generally regards staffing as the work of the personnel department, while the modern view holds that staffing should not only include selecting, evaluating, educating, but also how to use people and how to enhance organizational cohesion to retain people. This is closely linked to the guidance and leadership work.

PS plastic injection molding process characteristics and process parameter settings

1. PS is an amorphous plastic with a wide melting temperature range and good thermal stability;

2. The heat distortion temperature is 70-100 ° C, the viscous flow temperature is 150-204 ° C, and decomposition occurs above 300 ° C;

3, PS melt viscosity sensitivity to temperature and sensitivity to shear rate are moderate, good fluidity, easy to form;

4. The water absorption of the PS resin is very low, generally 0.01 to 0.03%, and it may not be dried before molding. [If necessary, it may be dried in a circulating hot air of 70 to 80 ° C for 2 to 3 hours].

5. The temperature of the barrel during injection molding is controlled within the range of 180 to 215 °C, and the nozzle temperature is 10 to 20 ° C lower than the maximum temperature of the barrel.

6, the injection pressure is generally controlled at 60 ~ 150MPa. Large gates, simple shapes and thick-walled products, the injection pressure can be lower, about 60 ~ 80MPa.

7, easy to form internal stress and cause cracking, residual stress problems are more prominent. In order to reduce the internal stress, a higher material temperature and a mold temperature are often required for processing, so that the melt is slowly cooled, and the oriented molecules are relaxed. It is also possible to select a grade with high fluidity or to add a flow aid

POM plastic injection molding process

1, plastic processing
POM has a small water absorption, generally 0.2%-0.5%. Under normal circumstances, POM can be processed without drying, but it must be dried for wet materials. The drying temperature is above 80 °C and the time is more than 2 hours. The specific conditions should be based on the supplier's data.
The proportion of recycled materials is generally not more than 20-30%. However, depending on the type of product and the end use, it can sometimes be up to 100%.

2, the selection of plastic machine
In addition to the requirement that the screw has no stagnant area, the POM has no special requirements for the injection molding machine, and generally can be injection molded.

3, mold and gate design
The common mold temperature is controlled to 80-90 ° C, the runner diameter is 3-6 mm, the gate length is 0.5 mm, the gate size depends on the thickness of the rubber wall, and the circular gate diameter should be at least 0.5-0.6 times the thickness of the product. The width of the rectangular gate is usually 2 times or more of the thickness, the depth is 0.6 times the wall thickness, and the draft angle is between 40' and 130'.

Exhaust system

POM-H thickness 0.01-0.02mm width 3mm

POM-K thickness 0.04mm width 3mm

4, the melting temperature
Available by airshot method

POM-H can be set to 215 ° C (190 ° C -230 ° C)

POM-K can be set to 205 ° C (190 ° C -210 ° C)

5, injection speed
    It is common for the medium speed to be too fast, too slow to produce ripples, too fast and easy to produce grain and shear overheating.

6, back pressure
The lower the better, generally no more than 200bar

POM injection molding process characteristics and process parameter settings

1. POM is also a typical heat-sensitive plastic, which will be seriously decomposed at 240 °C. At 210 ° C, the residence time should not exceed 20 min; even at 190 ° C, the residence time should preferably not exceed 1 h. Therefore, when molding, the lower molding temperature and shorter heating time should be selected as far as possible to ensure the fluidity of the material.

2. POM has a distinct melting point, a homopolymer POM of 175 ° C and a copolymerized POM of 165 ° C. At the time of molding, the distribution of the barrel temperature is 190 to 200 ° C in the front stage, 180 to 190 ° C in the middle stage, 150 to 180 ° C in the rear stage, and the nozzle temperature is 170 to 180 ° C. For thin-walled products, the barrel temperature can be increased as appropriate, but not more than 210 °C.

3. POM has low hygroscopicity and the resin may not be dried before processing. If necessary, it can be dried at 90 to 100 ° C for 2 to 4 hours.

4. The melt viscosity of POM is sensitive to shear rate. Therefore, in order to improve the melt fluidity, it is not possible to increase the temperature alone, but also to increase the injection rate and the injection pressure. For large gates, thick-walled short-flow processes, and small-area products, the injection pressure is 40-80 MPa; the general product is about 100 MPa. Small gate, thin wall long process, large area products, high injection pressure, 120 ~ 140MPa.

5, the mold temperature is usually controlled at 80 ~ 100 ° C, for thin-wall long process and complex shape of the product, the mold temperature can be increased to 120 ° C.

6. High crystallinity makes the molding shrinkage rate high (2~2.8%), and the wall thickness is prone to defects such as dents and shrinkage.

Black brown spot

Description: The molded part has the correct color tone but occasionally spots or streaks are visible.
Injection molding machine:
A. The degraded plastic in the last production operation is solidified in the gun screw and the rubber ring. -- Clean the injection unit with a cleaning mixture or high molecular weight acrylic.
B. The plastic is trapped in the “* corner” or no-flow area of the injection device, so that it stays too long at high temperatures. ————Removing the barrel and screw to thoroughly clean the surface in contact with the molten polymer; checking whether the nozzle is correctly located in the barrel; replacing the opening and closing nozzle with an open or straight type nozzle; Whether the head is broken.
C. The speed at which the plastic enters the mold cavity is too fast to cause excessive shearing of the aggregate. --- Reduce the injection speed.
D, the temperature of the melt is too high. ————Reducing the temperature of the barrel; checking whether the flow rate of the cooling body is sufficient for the hopper locking device, adjusting the flow rate if necessary; reducing the cycle time to increase the plastic passing through the injection device.
E. Incorrect screw surface speed and back pressure are used to cause excessive shearing of the molten plastic. ————Use minimum back pressure and correct screw surface speed
Mold:
A. Oil stains and oil appear in the mold. --- Remove the mold, especially the mouth, and clean it.
B. There are too few gates. ————— Increase the size of the gate.
C. The wall thickness of the injection molded parts is too thin, so that the plastic cannot flow sufficiently without degradation - check the correctness and consistency of the wall thickness.
D. Produce impurities in the hot runner mold - remove the hot nozzle